Key Differences
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 45,000 cps |
| Mix Ratio By Volume | 3A:1B | N/A (gram scale required) |
| Pot Life | 22 minutes | 45 minutes |
| Cure Time | 15 hours | 24 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 40 |
| Color | Clear Yellow | Mint Green |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAmite™ 102 | Mold Max™ 40 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 45,000 cps |
| Mix Ratio By Volume | 3A:1B | — |
| Mix Ratio By Weight | 100A:29B | 100A:10B |
| Pot Life | 22 minutes | 45 minutes |
| Thin Film Working Time | 90 minutes | — |
| Cure Time | 15 hours | 24 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 40 |
| Specific Gravity | 1.11 g/cc | 1.14 g/cc |
| Specific Volume | 25 cu. in./lb. | 24.3 cu. in./lb. |
| Color | Clear Yellow | Mint Green |
| Die B Tear Strength | — | 120 pli |
| Tensile Strength | — | 550 psi |
| Tensile Modulus | 450,000 psi | — |
| Ultimate Tensile | 8,180 psi | — |
| Tensile Elongation | 3.15 % | — |
| Elongation @ Break | — | 250 % |
| 100% Modulus | — | 190 psi |
| Compressive Strength | 10,970 psi | — |
| Compressive Modulus | 122,000 psi | — |
| Flexural Strength | 12,220 psi | — |
| Flexural Modulus | 423,000 psi | — |
| Shrinkage | — | 0.004 in. / in. |
| Heat Deflection Temp | 120 °F | — |
| Useful Temperature (min) | — | -65 °F |
| Useful Temperature (max) | — | 400 °F |
| Dielectric Constant, 100Hz | — | 3.29 |
| Dielectric Strength | — | 330 volts/mil |
| Dissipation Factor, 100Hz | — | 0.005 |
| Flexural Strength on 6 ply / 10 oz. Laminate | 28,500 psi | — |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 26,800 psi | — |
| Volume Resistance | — | 8.29E+11 ohm |
| Volume Resistivity | — | 5.83E+13 ohm/cm |
Product Description
EpoxAmite™ 102
EpoxAmite™ 102 is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite™ 102 includes the EpoxAmite™ 100 Base and the EpoxAmite™ 102 MEDIUM Hardener. EpoxAmite™ 102 is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.
EpoxAmite™ 102 can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite™ 102 can also be mixed with fillers such as fumed silica for gel coat applications. Urefil™ 3, Urefil™ 7 and other fillers can be added for fairing, filleting or bonding applications.
Applications: Wet Lay-Up Lamination, General Bonding & Repair, Clear Coating - Gel Coating, Barrier Coating, Thin-Section Casting, Water Proofing, Patching & Small Laminates
Also available: EpoxAmite™ 101 FAST SET and EpoxAmite™ 103 SLOW SET
Mold Max™ 40
Mold Max™ Silicones are tin-cured silicone mold rubber compounds that have exceptional working properties and library life. Mold Max™ Silicones feature Smooth-On’s exclusive “Libra™” catalyst for long library life. Mold Max™ silicones can be pigmented with Silc Pig™ silicone colorants. Pot life for the pourable silicones is 45 minutes and they cure overnight at room temperature.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.