Key Differences
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 1,200 cps |
| Pot Life | 22 minutes | 13 minutes |
| Cure Time | 15 hours | 24 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 80 |
| Color | Clear Yellow | Translucent |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAmite™ 102 | Econ™ 80 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 1,200 cps |
| Mix Ratio By Volume | 3A:1B | 1A:1B |
| Mix Ratio By Weight | 100A:29B | 100A:90B |
| Pot Life | 22 minutes | 13 minutes |
| Thin Film Working Time | 90 minutes | — |
| Handling Time | — | 6 hours |
| Cure Time | 15 hours | 24 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 80 |
| Specific Gravity | 1.11 g/cc | 1.06 g/cc |
| Specific Volume | 25 cu. in./lb. | 26.16 cu. in./lb. |
| Color | Clear Yellow | Translucent |
| Die C Tear Strength | — | 77 pli |
| Tensile Strength | — | 955 psi |
| Tensile Modulus | 450,000 psi | — |
| Ultimate Tensile | 8,180 psi | — |
| Tensile Elongation | 3.15 % | — |
| Elongation @ Break | — | 127 % |
| 100% Modulus | — | 670 psi |
| Compressive Strength | 10,970 psi | — |
| Compressive Modulus | 122,000 psi | — |
| Flexural Strength | 12,220 psi | — |
| Flexural Modulus | 423,000 psi | — |
| Shrinkage | — | 0.0014 in. / in. |
| Heat Deflection Temp | 120 °F | — |
| Flexural Strength on 6 ply / 10 oz. Laminate | 28,500 psi | — |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 26,800 psi | — |
Product Description
EpoxAmite™ 102
EpoxAmite™ 102 is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite™ 102 includes the EpoxAmite™ 100 Base and the EpoxAmite™ 102 MEDIUM Hardener. EpoxAmite™ 102 is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.
EpoxAmite™ 102 can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite™ 102 can also be mixed with fillers such as fumed silica for gel coat applications. Urefil™ 3, Urefil™ 7 and other fillers can be added for fairing, filleting or bonding applications.
Applications: Wet Lay-Up Lamination, General Bonding & Repair, Clear Coating - Gel Coating, Barrier Coating, Thin-Section Casting, Water Proofing, Patching & Small Laminates
Also available: EpoxAmite™ 101 FAST SET and EpoxAmite™ 103 SLOW SET
Econ™ 80
Econ™ 80 is an economical Shore 80A urethane rubber suitable for a variety of mold making and industrial applications. It is a lower cost, faster cure alternative to our popular PMC™-780. Physical properties are lower vs. PMC™-780. This is a no odor system that features a 1A:1B mix ratio and a low viscosity for easy mixing and pouring. Working time is about 13 minutes at room temperature, handling time is 6 hours and rubber cures overnight. Econ™ 80 is translucent and easily colored with SO-Strong™ or Ignite™ colorants. Econ™ 80 is used to make short run molds for casting concrete and resins, concrete stamping pads, rubber mechanical parts, coating fabrics, pour-in-place gaskets for industrial equipment and burial vaults. Important: To minimize air bubbles in cured rubber, vacuum degassing is recommended.
FOR COMMERCIAL/INDUSTRIAL USE ONLY