C
mpare
T
l
Key Differences
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 250 cps |
| Mix Ratio By Volume | 3A:1B | N/A (gram scale required) |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 50 |
| Color | Clear Yellow | Clear |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAmite™ 102 | Clear Flex™ 50 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 250 cps |
| Mix Ratio By Volume | 3A:1B | — |
| Mix Ratio By Weight | 100A:29B | 1A:2B |
| Pot Life | 22 minutes | 25 minutes |
| Thin Film Working Time | 90 minutes | — |
| Cure Time | 15 hours | 16 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 50 |
| Specific Gravity | 1.11 g/cc | 1.04 g/cc |
| Specific Volume | 25 cu. in./lb. | 26.8 cu. in./lb. |
| Color | Clear Yellow | Clear |
| Die C Tear Strength | — | 25 pli |
| Tensile Strength | — | 250 psi |
| Tensile Modulus | 450,000 psi | — |
| Ultimate Tensile | 8,180 psi | — |
| Tensile Elongation | 3.15 % | — |
| Elongation @ Break | — | 500 % |
| Compressive Strength | 10,970 psi | — |
| Compressive Modulus | 122,000 psi | — |
| Flexural Strength | 12,220 psi | — |
| Flexural Modulus | 423,000 psi | — |
| Shrinkage | — | 0.0015 in. / in. |
| Heat Deflection Temp | 120 °F | — |
| Flexural Strength on 6 ply / 10 oz. Laminate | 28,500 psi | — |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 26,800 psi | — |
Product Description
EpoxAmite™ 102
EpoxAmite™ 102 is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite™ 102 includes the EpoxAmite™ 100 Base and the EpoxAmite™ 102 MEDIUM Hardener. EpoxAmite™ 102 is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.
EpoxAmite™ 102 can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite™ 102 can also be mixed with fillers such as fumed silica for gel coat applications. Urefil™ 3, Urefil™ 7 and other fillers can be added for fairing, filleting or bonding applications.
Applications: Wet Lay-Up Lamination, General Bonding & Repair, Clear Coating - Gel Coating, Barrier Coating, Thin-Section Casting, Water Proofing, Patching & Small Laminates
Also available: EpoxAmite™ 101 FAST SET and EpoxAmite™ 103 SLOW SET
Clear Flex™ 50
Clear Flex™ 50 is a water white clear urethane liquid rubber compounds designed for applications that require absolute clarity and resistance to sunlight. Low viscosity ensures easy mixing and pouring. Clear Flex™ 50 will cure at room temperature with negligible shrinkage.
CAUTION: NOT FOR HOME USE. THIS PRODUCT IS FOR INDUSTRIAL USE ONLY. With adequate local exhaust ventilation, respiratory protection is not normally required when using this product. Where risk assessment shows air-purifying respirators are appropriate, follow OSHA respirator regulations and European Standards EN 141, 143 and 371. Protective clothing (gloves and long sleeves) is required to minimize the risk of dermal sensitization. If breathing is affected or a dermal rash develops, immediately cease using this product and seek medical attention. Read SDS before using.