| EpoxAmite™ 102 | |
|---|---|
| Product Type |
|
| Mixed Viscosity | 650 cps |
| Mix Ratio By Volume | 3A:1B |
| Mix Ratio By Weight | 100A:29B |
| Pot Life | 22 minutes |
| Thin Film Working Time | 90 minutes |
| Cure Time | 15 hours |
| Shore D Hardness | 80 |
| Specific Gravity | 1.11 g/cc |
| Specific Volume | 25 cu. in./lb. |
| Color | Clear Yellow |
| Tensile Modulus | 450,000 psi |
| Ultimate Tensile | 8,180 psi |
| Tensile Elongation | 3.15 % |
| Compressive Strength | 10,970 psi |
| Compressive Modulus | 122,000 psi |
| Flexural Strength | 12,220 psi |
| Flexural Modulus | 423,000 psi |
| Heat Deflection Temp | 120 °F |
| Flexural Strength on 6 ply / 10 oz. Laminate | 28,500 psi |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 26,800 psi |
Product Description
EpoxAmite™ 102
EpoxAmite™ 102 is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite™ 102 includes the EpoxAmite™ 100 Base and the EpoxAmite™ 102 MEDIUM Hardener. EpoxAmite™ 102 is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.
EpoxAmite™ 102 can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite™ 102 can also be mixed with fillers such as fumed silica for gel coat applications. Urefil™ 3, Urefil™ 7 and other fillers can be added for fairing, filleting or bonding applications.
Applications: Wet Lay-Up Lamination, General Bonding & Repair, Clear Coating - Gel Coating, Barrier Coating, Thin-Section Casting, Water Proofing, Patching & Small Laminates
Also available: EpoxAmite™ 101 FAST SET and EpoxAmite™ 103 SLOW SET