C
mpare
T
l
Key Differences
| Product Type |
|
|
| Mixed Viscosity | 13,000 cps | 2,800 cps |
| Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
| Pot Life | 1 minute | 62 minutes |
| Cure Time | 5 minutes | 24 hours |
| Shore D Hardness | — | 85 |
| Shore A Hardness | 5 | — |
| Color | Translucent | White |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| Ecoflex™ 5 | EpoxAmite™ WHITE 102 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 13,000 cps | 2,800 cps |
| Mix Ratio By Volume | 1A:1B | — |
| Mix Ratio By Weight | 1A:1B | 100A:23B |
| Pot Life | 1 minute | 62 minutes |
| Thin Film Working Time | — | 120 minutes |
| Cure Time | 5 minutes | 24 hours |
| Shore D Hardness | — | 85 |
| Shore A Hardness | 5 | — |
| Specific Gravity | 1.07 g/cc | 1.23 g/cc |
| Specific Volume | 25.8 cu. in./lb. | 22.5 cu. in./lb. |
| Color | Translucent | White |
| Die B Tear Strength | 75 pli | — |
| Tensile Strength | 350 psi | — |
| Tensile Modulus | — | 557,000 psi |
| Ultimate Tensile | — | 5,600 psi |
| Tensile Elongation | — | 1.2 % |
| Elongation @ Break | 1,000 % | — |
| 100% Modulus | 15 psi | — |
| Compressive Strength | — | 11,960 psi |
| Compressive Modulus | — | 114,000 psi |
| Flexural Strength | — | 8,350 psi |
| Flexural Modulus | — | 446,000 psi |
| Shrinkage | <.001 in. / in. | — |
| Heat Deflection Temp | — | 133 °F |
| Useful Temperature (min) | -65 °F | — |
| Useful Temperature (max) | 450 °F | — |
| Flexural Strength on 6 ply / 10 oz. Laminate | — | 31,600 psi |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | — | 30,700 psi |
Product Description
Ecoflex™ 5
Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.
EpoxAmite™ WHITE 102
EpoxAmite™ White Epoxy Laminating System is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite™ White Laminating System is odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.
EpoxAmite™ White Laminating System can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up& applications or composite parts. EpoxAmite™ White Resin can also be mixed with fillers such as fumed silica for gel coat applications. Urefil™ 3, Urefil™ 7 and other fillers can be added for fairing, filleting or bonding applications.