| Mixed Viscosity | 13,000 cps | 8,000 cps |
| Pot Life | 1 minute | 18 minutes |
| Cure Time | 5 minutes | 3 hours |
| Shore A Hardness | 5 | 00-50 |
| Die B Tear Strength | 75 pli | 50 pli |
| Ecoflex™ 5 | Ecoflex™ 00-50 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 13,000 cps | 8,000 cps |
| Mix Ratio By Volume | 1A:1B | 1A:1B |
| Mix Ratio By Weight | 1A:1B | 1A:1B |
| Pot Life | 1 minute | 18 minutes |
| Cure Time | 5 minutes | 3 hours |
| Shore A Hardness | 5 | 00-50 |
| Specific Gravity | 1.07 g/cc | 1.07 g/cc |
| Specific Volume | 25.8 cu. in./lb. | 25.9 cu. in./lb. |
| Color | Translucent | Translucent |
| Die B Tear Strength | 75 pli | 50 pli |
| Tensile Strength | 350 psi | 315 psi |
| Elongation @ Break | 1,000 % | 980 % |
| 100% Modulus | 15 psi | 12 psi |
| Shrinkage | <.001 in. / in. | <.001 in. / in. |
| Useful Temperature (min) | -65 °F | -65 °F |
| Useful Temperature (max) | 450 °F | 450 °F |
Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.
Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing, or you can choose to mix and dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.